Urmila R. Kawade, Deepak G B, Anand B3, Lakshmi H S, Pradeep C R, Prashant Sunagar, Jagadish Vengala, "Multi-Objective Optimization of GGBS Blended Pervious Concrete: Coupling Mechanical Strength, Permeability, and Water Purification via Microstructure Control," International Journal of Civil Engineering, vol. 13, no. 8, pp. 450-468, 2026. Crossref, https://doi.org/10.14445/23488352/IJCE-V13I8P127

Abstract

This study extends the design space of pervious concrete with respect to strength, drainage, and water purification using a multi-objective optimization approach. GGBS was used as a partial cement replacement (15–45%) across four no-fines coarse-aggregate gradations and assessed for compressive strength (accelerated, 7-day, and 28-day), constant and falling head permeability, and water filtration. The optimal formulation - a 60:40 blend by mass of the 16–10 mm and 10–4.75 mm coarse-aggregate fractions, with 30% GGBS - develops a compressive strength of 11.78 MPa at 7 days rising to 18.83 MPa at 28 days, together with a measured permeability coefficient of 2.0 mm/s and removals of 23.8% of dissolved solids and 10.2% of suspended solids. Microstructural images from SEM and porosity specifications indicate that slag modification densifies the interfacial transition zone without impeding drainage. Structure–property relationships align with previous studies indicating the presence of a design space with an optimal strength target for multifunctional properties. This evidence demonstrates that microstructural optimization via slag enables simultaneous structural and environmental performance, thereby promoting the use of pervious concrete in urban infrastructures.

Keywords

Pervious concrete, Multi-objective optimization, Aggregate gradation, Water purification, Permeability.

References

1. Hilal El-Hassan, and Peiman Kianmehr, “Pervious Concrete Pavement Incorporating GGBS to Alleviate Pavement Runoff and Improve Urban Sustainability,” Road Materials and Pavement Design, vol. 19, no. 1, pp. 167-181, 2018.
   [CrossRef] [Google Scholar] [Publisher Link]
2. Yanchen Oinam et al., “Characteristics of GGBFS-based Pervious Concrete Considering Rheological Properties of the Binder,” International Journal of Concrete Structures and Materials, vol. 16, no. 1, pp. 1-14, 2022.
   [CrossRef] [Google Scholar] [Publisher Link]
3. Bright Singh Seeni et al., “Performance of Pervious Concrete with Ground Granulated Blast Furnace Slag (GGBS) as Partial Replacement for Cement,” Transportation in Developing Economies, vol. 11, no. 1, 2025.
   [CrossRef] [Google Scholar] [Publisher Link]
4. Xiwen Yan et al., “Performance Analysis and Admixture Optimization of GBFS-HPMC/Fiber Pervious Concrete,” Materials, vol. 16, no. 19, pp. 1-22, 2023.
   [CrossRef] [Google Scholar] [Publisher Link]
5. Jawad Ahmad et al., “A Comprehensive Review on the Ground Granulated Blast Furnace Slag (GGBS) in Concrete Production,” Sustainability, vol. 14, no. 14, pp. 1-27, 2022.
   [CrossRef] [Google Scholar] [Publisher Link]
6. Sandeep Sathe, and Shahbaz Dandin, “Experimental Study of Permeable Concrete with FA and GGBS as Partial Replacement to Cement,” European Journal of Environmental and Civil Engineering, vol. 29, no. 5, pp. 832-858, 2025.
   [CrossRef] [Google Scholar] [Publisher Link]
7. Shaofeng Zhang et al., “Insight into Mechanical Properties and Microstructure of Concrete Containing Steel Slag and Ground-Granulated Blast-Furnace Slag,” Journal of Sustainable Cement-Based Materials, vol. 12, no. 9, pp. 1169-1180, 2023.
   [CrossRef] [Google Scholar] [Publisher Link]
8. Wei Chen, Mengmeng Wu, and Yue Liang, “Effect of SF and GGBS on Pore Structure and Transport Properties of Concrete,” Materials, vol. 17, no. 6, pp. 1-21, 2024.
   [CrossRef] [Google Scholar] [Publisher Link]
9. Bahador Sabet Divsholi, Tze Yang Darren Lim, and Susanto Teng, “Durability Properties and Microstructure of Ground Granulated Blast Furnace Slag Cement Concrete,” International Journal of Concrete Structures and Materials, vol. 8, no. 2, pp. 157-164, 2014.
   [CrossRef] [Google Scholar] [Publisher Link]
10. Edgar Yurihuaman et al., “Influence of Blast Furnace Slag on Concrete: Mechanical Strength and Microstructural Characterization,” Civil Engineering Journal, vol. 11, no. 8, pp. 3069-3090, 2025.
    [CrossRef] [Google Scholar] [Publisher Link]
11. Bashdar Omer et al., “Evaluating the Long-Term Strength of GGBFS-blended Cement Across Various Water-to-Binder and Superplasticizer Ratios under Heating/Cooling Cycles,” PLOS ONE, vol. 20, no. 11, pp. 1-31, 2025.
    [CrossRef] [Google Scholar] [Publisher Link]
12. Akram O. Kadhum et al., “High-Performance Eco-Friendly Concrete with Improved Strength, Chloride Ion Penetration, and Corrosion Resistance by the High Volume of Ground Granulate Blast Furnace Slag (GGBS),” Materials Protection, vol. 66, no. 4, pp. 845-866, 2025.
    [CrossRef] [Google Scholar] [Publisher Link]
13. Mohamad Ali-Ahmad et al., “Experimental Evaluation of Fresh, Mechanical, Durability-Related and Microstructural Properties of Concrete Incorporating GGBS and EAF Slag Aggregate,” Results in Engineering, vol. 30, pp. 1-13, 2026.
    [CrossRef] [Google Scholar] [Publisher Link]
14. Xixuan Bai et al., “Compressive Strength, Permeability, and Abrasion Resistance of Pervious Concrete Incorporating Recycled Aggregate,” Sustainability, vol. 16, no. 10, pp. 1-16, 2024.
    [CrossRef] [Google Scholar] [Publisher Link]